1 DiabloCanyonNPEm Resource From: Ferrer, Nathaniel Sent: Tuesday, July 06, 2010 4:18 PM To: Grebel, Terence; Soenen, Philippe R Cc: Green, Kimberly; DiabloHearingFile Resource
Subject:
Draft RAI Set 15 - AMR and AMP RAIs Attachments:
Draft RAI Set 15 AMR and AMP RAIs.docTerry and Philippe, Attached is Draft RAI Set 15 containing draft RAIs, specifically on portions of the aging management review and aging management programs. Please review the attached draft RAIs and let me know if and when you would like to have a teleconference call. The purpose of the call will be to obtain clarification on the staff's request.
Please let me know if you have any questions.
NathanielFerrerProjectManagerDivisionofLicenseRenewalOfficeofNuclearReactorRegulationU.S.NuclearRegulatoryCommission(301)415 1045 Hearing Identifier: DiabloCanyon_LicenseRenewal_NonPublic Email Number: 1952 Mail Envelope Properties (26E42474DB238C408C94990815A02F090A76D411C5)
Subject:
Draft RAI Set 15 - AMR and AMP RAIs Sent Date: 7/6/2010 4:18:11 PM Received Date: 7/6/2010 4:18:12 PM From: Ferrer, Nathaniel Created By: Nathaniel.Ferrer@nrc.gov Recipients: "Green, Kimberly" <Kimberly.Green@nrc.gov>
Tracking Status: None "DiabloHearingFile Resource" <DiabloHearingFile.Resource@nrc.gov> Tracking Status: None "Grebel, Terence" <TLG1@PGE.COM> Tracking Status: None "Soenen, Philippe R" <PNS3@PGE.COM> Tracking Status: None
Post Office: HQCLSTR01.nrc.gov Files Size Date & Time MESSAGE 594 7/6/2010 4:18:12 PM Draft RAI Set 15 AMR and AMP RAIs.doc 52730 Options Priority: Standard Return Notification: No Reply Requested: No Sensitivity: Normal Expiration Date: Recipients Received:
Diablo Canyon Nuclear Power Plant, Units 1 and 2 (DCPP) License Renewal Application (LRA) Draft Request for Additional Information Set 15 Aging Management Review/Aging Management Programs D-RAI 3.1.2.3.2-1 In LRA Tables 3.1.2-2, 3.3.2-8, and 3.3.2-17 the applicant stated that carbon steel tanks, heaters, and valve internal surfaces exposed to treated borated water can experience loss of material, and that the Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program will be used to manage this aging effect. The AMR line items cite generic note G, indicating that the environment is not in the GALL Report for this component and material combination. The AMR line item in Table 3.1.2-2 also cites a plant specific note indicating that the tank has an internal coating that is not credited for aging management. The AMR line item in Table 3.3.2-8 also cites a plant specific note indicating that the component is a flange separated from the treated borated water by a gasket.
The Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components program involves visual inspections of internal surfaces of steel piping, piping elements, ducting, and components in an internal environment (such as indoor uncontrolled air, condensation, and steam). It is unclear to the staff how the Internal Surfaces in Miscellaneous Piping and Ducting Components program is adequate to manage loss of material for the carbon steel tanks, heaters, and valve internal surfaces exposed to treated borated water discussed above.
Provide justification for why the Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program is acceptable to manage loss of material in the identified carbon steel tanks, heaters, and valves exposed to treated borated water.
D-RAI 3.3.2.2.4-1 LRA Table 3.3.1, Item 3.3.1.08 addresses stainless steel PWR regenerative heat exchanger components exposed to treated borated water greater than 60°C (140
°F), which are being managed for cracking due to stress corrosion cracking and cyclic loading. The SRP-LR recommends the use of the Water Chemistry Program to manage the effect of cracking due to SCC. In addition, the SRP-LR recommends a plant-specific aging management program to verify the absence of cracking due to SCC and cyclic loading and ensure that these aging effects are managed adequately. The applicant proposes to manage this aging effect using its Water Chemistry Program (B2.1.2) and One-Time Inspection Program (B2.1.16).
The applicant states that its One-Time Inspection will include selected components at susceptible locations. However, the applicant does not identify the technique to be used to perform the proposed inspections on heat exchanger components.
Describe the details of the inspection technique to be used to perform the one-time inspection of these heat exchanger components and provide relevant plant or industry experience to demonstrate the effectiveness and reliability of the technique.
D-RAI 3.4.2.1-1 SRP-LR Table 3.4-1, items 2 and 3, state that steel piping, piping components, piping elements, and heat exchanger components exposed to steam or treated water are subject to loss of material due to general, pitting, and crevice corrosion. The GALL Report, under items VIII.A-16 and VIII.E-37, recommends managing the aging effect using the Water Chemistry and One-
Time Inspection Programs.
The LRA Table 3.4.2-4 indicates that carbon steel heat exchanger components exposed to secondary water or steam in the condensate system can undergo loss of material, and the Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program will be used to manage this aging effect. The AMR line items cite generic note E, indicating that they are consistent with the GALL Report for material, environment and aging effect, but that a different aging management program is credited. The LRA references the GALL Report items VIII.A-16 and VIII.E-37 for this aging issue, and notes that the use of the Water Chemistry and the One-Time Inspection Programs were not considered appropriate to manage wall thickness reductions of the main condenser shell and hotwell internal surfaces exposed to treated water and steam environment due to DCPP operating experience supporting anticipated condenser wall thickness reduction. The LRA states that the Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program is consistent with exceptions to the corresponding AMP XI.M38 in the GALL Report. Although the exception pertaining to inspection techniques indicates that volumetric testing may be performed on stainless steel to detect stress corrosion cracking, visual inspections only will be used to detect loss of material in carbon steel. Since visual inspections alone may not be effective in identifying loss of material due to general corrosion, and the DCPP operating experience pertaining to condenser wall thickness reduction is not further described, the staff is unclear on how the use of the Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program will be able to manage this aging effect.
Describe how the credited AMP is adequate to manage the loss of material due to general, pitting, and crevice corrosion of the car bon steel heat exchanger components exposed to secondary water or steam in the condensate system.
D-RAI 3.4.2.1-2
SRP-LR Table 3.4-1, item 16, states that stainless steel piping, piping components, piping elements, tanks, and heat exchanger components exposed to treated water are subject to loss of material due to pitting and crevice corrosion. The GALL Report, under item VIII.B1-4, recommends managing the aging effect using the Water Chemistry and One-Time Inspection
Programs.
The LRA Table 3.4.2-2 indicates that stainless steel piping exposed to secondary water in the auxiliary steam system can undergo loss of material, and the Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program will be used to manage this aging effect for stainless steel piping in the auxiliary steam system. The AMR line item cites generic note E, indicating that they are consistent with the GALL Report item for material, environment, and aging effect, but a different aging management program is credited. The LRA references the GALL Report item VIII.B1-4 for this aging issue, and notes that the Water Chemistry Program does not apply because the associated component is abandoned in place. Since the current AMP will use preventive maintenance and surveillance activities to conduct and document inspections, the staff is unclear how the use of the Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program will be able to manage this aging effect. Describe how the credited AMP, which uses preventive maintenance and surveillance activities to conduct and document inspections, is adequate to manage the loss of material due to pitting and crevice corrosion of the stainless steel piping exposed to secondary water in the auxiliary steam system, which has been abandoned in-place.
D-RAI B2.1.22-3 The GALL AMP XI.M38, "Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components," "detection of aging effects" program element, recommends that locations for inspection should be chosen to include conditions likely to exhibit the aging effects and that the inspection intervals should be established such that they provide for timely detection of degradation. LRA AMP B2.1.22, "Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program," states that the program "-will provide for periodic inspection of a representative sample of the internal surfaces material and environment combinations for systems within the scope of the program."
Although LRA AMP B.2.1.22 requires the periodic inspection of a representative sample of the internal surfaces material and environment combinations for systems within the scope of the program, the program does not clearly establish how the sampling would be accomplished.
Describe the sampling methodology, including how the population for each of the material-environment-aging effect combinations is being selected, and what type of engineering, design, or operating experience considerations would be used to select the sample of components for both the scheduled and supplemental inspections.
D-RAI B2.1.22-4 The GALL XI.M38, "Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components," "detection of aging effects" program element, recommends that the applicant should identify and justify the inspection technique for the aging effect of concern. In LRA AMP B2.1.22, "Inspection of Internal Surfaces in Miscellaneous Piping and Ducting Components Program," the applicant took an exception to the "scope of program" and "detection of aging effects," program elements and stated that the proposed AMP will also manage aging effects in asbestos cement pipes (ACP) through visual inspections of their internal surfaces. LRA Tables 3.3.2-5 and 3.3.2-12 for this material in a raw water environment describe the aging effects to be loss of material, cracking, and changes in material properties.
In the LRA, the applicant identified visual inspections to be the technique used to manage the aging effects of concern (i.e., loss of material, cracking, and changes in material properties) for ACPs. Performing visual inspections of the internal surfaces of ACPs may not be adequate to detect changes in the cementitious material properties.
Provide the basis for concluding that visual inspections can be effectively used to identify changes in ACP material properties. If available, also provide examples of plant-specific operating experience that could be used to demonstrate the effectiveness of visual inspections as a means of identifying changes in ACP material properties.