ML19211C685
| ML19211C685 | |
| Person / Time | |
|---|---|
| Site: | Maine Yankee |
| Issue date: | 12/31/1979 |
| From: | Grier B NRC OFFICE OF INSPECTION & ENFORCEMENT (IE REGION I) |
| To: | Groce R Maine Yankee |
| References | |
| NUDOCS 8001140215 | |
| Download: ML19211C685 (1) | |
Text
'
- o, UNITED STATES 8
NUCLEAR REGULATORY COMMISS!ON o
3 j
REGION I O,
g M1 PARK AVENUE U
o KING oP PRUSSIA. PENNSYLVANIA 19406 Docket No. 50-309 DEC 311979 Maine Yankee Atomic Power Company ATTN:
Mr. Robert H. Groce Licensing Engineer 20 Turnpike Road Westborough, Massachusetts 01581 Gentlemen:
This Information Notice is provided as an early.1otificatf or, of a possibly significant matter.
It is expected that recipients will review the infor-mation for possible applicability to their facilities.
No specific action or response is requested at this time.
If NRC evaluations so indicate, furtner licensee actions may be requested or required.
If you have questions regarding this matter, please contact this office.
Sincerely, I' //f
)
/Boyce H. Grier Director
Enclosures:
1.
IE Information Notice No. 79-37 with attachments 2.
List of Recently Issued IE Information Notices CONTACT:
L. E. Tripp (215-337-5282) cc w/encls:
E. Wood, Plant Superintendent E. W. Thurlow, President 1738 001 80011402l5
ENCLOSURE 1 UNITED STATES ISINS NO.:
6870 NUCLEAR REGULATORY COMMISSION Accession No.:
OFFICE OF INSPECTION AND ENFORCEMENT 7910250525 WASHINGTON, D.C.
20555 IE Information Notice No. 79-37 Date:
December 33, 1979 Pace 1 of 2 CRACKING IN LOW PRESSURE TURBINE DISCS Description of Circumstances:
An anonymous letter was received by the Director of the Office of Inspection and Enforcement, on November 17, 1979 which alleged possible violation of Part 10 CFR 50.55(e) and/or 10 CFR 21 Regulations concerning reportability of recently discovered stress corrosion cracking in Westirghouse 1800 rpm low pressure turbine discs.
Westinghouse had made a presentation on the turbine disc cracking to electric utility executives on October 30, 1979.
Telephone discussions between the NRC staff and Westinghouse's Turbine Division on No<+ ter 20, 1979 established that cracking, attributed to stress corrosion phenomena, had been found in the keyway areas of several LP turbine discs at operating plants and that inservice inspection techniques (i.e., in situ ultra-sonic examination) for crack detection have been developed and are being imple-mentad in the field.
The Office of Inspection and Enforcement was also notified on bovember 20, 1979 that during the current overhaul of Commonwealth Edison's Zion Unit 1 LP turbine, ultrasonic examination revealed embedded cracks located on he inlet side on the disc bore area where no cracks had been previcusly observed.
Ultrasonic measurements indicate this disc bore cracking is of greater depth than the keyway cracks found to date.
According to Westinghouse, these bore cracks have been metallurgically examined and preliminary findings show them not to be typical of classical stress corrosion cracking observed in the keyways.
The probable cracking mechanism and impact on disc integrity is being further evaluated by Westinghouse.
A meeting was held on December 17, 1979 between tha NRC staff, Westinghouse and utility representatives to discuss the disc cracking problem, repair alter-natives, turbine missile evaluation, inspection techniques and plant inspection priorities.
In response to the staffs' request, Westinghouse provided the staff an updated report on December 21, 1979 regarding the current field inspection program that included a list of nuclear power plants already inspected, recom-mended inspection schedules and pertinent information related to LP turbines where cracks have been observed.
Inspections to date have id disc cracks at Surry Unit 2, Point Bea and Zion Unit 1.
All units except Poi the plants return to power.
Point Beac with a small crack in the No. 2 disc of DUPLICATE DOCUMENT Westinghouse indicated that the observe during 28 additional months of turbine Entire document previously the turbine inspection results and anal; entered into system under: