L-03-010, Proposed Alternatives to Gas-Tungsten Arc Welding (Relief Request BV3-RV-03)

From kanterella
Jump to navigation Jump to search
Proposed Alternatives to Gas-Tungsten Arc Welding (Relief Request BV3-RV-03)
ML030780290
Person / Time
Site: Beaver Valley
Issue date: 03/17/2003
From: Bezilla M
FirstEnergy Nuclear Operating Co
To:
Document Control Desk, Office of Nuclear Reactor Regulation
References
BV3-RV-03, L-03-010
Download: ML030780290 (28)
v • d • e


Text

FENOC

""-A%

Beaver Valley Power Station PO Box 4 FirstEnergy NuclearOperatingCompany Shippingport.PA 15077-0004 724-682-5234 Mark B Bezilla Fax 724-643-8069 Vice President March 17, 2003 L-03-010 U. S. Nuclear Regulatory Commission Attention: Document Control Desk Washington, DC 20555-0001

Subject:

Beaver Valley Power Station, Unit No. 1 and No. 2 BV-1 Docket No. 50-334, License No. DPR-66 BV-2 Docket No. 50-412, License No. NPF-73 Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW)

Machine Temper Bead Welding Requirements (Relief Request BV3-RV-03)

Pursuant to 10 CFR 50.55a(a)(3)(i), BVPS is proposing alternatives to the gas-tungsten arc welding (GTAW) machine temper bead welding requirements of IWA-4500 and IWA-4530 of ASME Section XI. This request is for Beaver Valley Power Station (BVPS) Units 1 and 2 during the third and second 10-Year intervals, respectively, of the Inservice Inspection Program.

Specifically, BVPS is requesting authorization to use an ambient temperature automatic or machine GTAW temper bead process for certain repairs to J-groove welds on the Reactor Vessel Head Penetrations. The repair welds performed using an ambient temperature temper bead procedure, which utilizes an automatic or machine GTAW process exhibits mechanical properties equivalent to or better than those of the surrounding base material. This relief request is based on the technical justification provided in the enclosure to this letter.

Should BVPS identify the need to perform repairs using the embedded flaw repair technique during the 1R15 refueling outage which began on March 8, 2003, BVPS may request expedited approval of these Code alternative requests.

Beaver Valley Power Station, Unit No. 1 and No. 2 Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements (Relief Request BV3-RV-03)

L-03-010 Page 2 No new commitments are contained in this submittal. If there are any questions regarding this matter, please contact Mr. Larry R. Freeland, Manager, Regulatory Affairs/Performance Improvement at 724-682-5284.

Sincerely, Mark B. Bezilla Enclosure c: Mr. T. G. Colburn, NRR Project Manager Mr. D. M. Kern, NRC Sr. Resident Inspector Mr. H. J. Miller, NRC Region I Administrator

ENCLOSURE Proposed Alternatives To The Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Relief Request No. BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Relief Request BV3-RV-03 I. ASME Code Component(s) Affected Component number: B4.12, B4.11

==

Description:==

Control Rod Drive Mechanism nozzle penetration (65)

Reactor Head Vent nozzle penetration (1)

Code Class: 1 II. Applicable Code Addition and Addenda The American Society of Mechanical Engineers (ASME) Code,Section XI, 1989 Edition.

Construction code for BVPS Units 1 and 2: ASME Section III, 1971 Edition, 1973 Winter Addenda.

Applicable component construction codes:

BVPS 1 - Reactor Vessel -- ASME Section III, Class A, 1968 Edition, Winter 1968 Addenda.

BVPS 1 - Full and Part length CRDM Housings -- ASME Section III, Class A, 1968 Edition, Winter 1969 Addenda BVPS 2- Reactor Vessel -- ASME Section III, 1971 Edition, Summer 1972 Addenda I1l. Applicable Code Requirement Subarticle IWA-4120(a) of ASME Section Xl, 1989 Edition, states:

"Repairs and installation of replacement items shall be performed in accordance with the Owner's Design Specification and the original Construction Code of the component or system. Later editions and Addenda of the Construction Code or of Section III, either in their entirety or portions thereof, and Code Cases may be used. If repair welding cannot be performed in accordance with these requirements, the applicable alternative requirements of IWA-4500 may be used."

ASME Section XI, 1989 Edition, IWA 4120 (b) states, "The Edition and Addenda of Section XI used for the repair program shall correspond with the Edition and Addenda identified in the inservice inspection program applicable to the inspection interval." In addition, IWA 4120 (c) of the same Edition and Addenda states, "Later Editions and Addenda of Section XI, either in their entirety or portions thereof, may be used for the repair program, provided these Editions and Addenda of Section XI at the time of the planned repair have been incorporated by reference in amended regulations of the regulatory authority having jurisdiction at the plant site. BVPS requests approval for the use of portions of ASME XI, 1989 Edition, 1991 Addenda, the use of Code case N638, and the alternative methods listed below, as applicable, to complete VHP repairs during Page 1 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements the spring 2003 outage and for the remaining life of the BVPS-1 existing Reactor head component.

IWA-4500 of ASME Section Xl, 1989 Edition, 1991 Addenda, establishes alternative repair welding methods for performing temper bead welding. According to IWA 4500(a), "Repairs to base materials and welds identified in IWA-4510, IWA-4520, and IWA-4530 may be made by welding without the specified postweld heat treatment requirements of the Construction Code or Section III, provided the requirements of IWA 4500(a) through (e) and IWA-451 0, IWA-4520, or IWA-4530, as applicable, are met."

IWA-4530 applies to dissimilar materials such as welds that join P-Number 43 nickel alloy to P-Number 3 low alloy steels. According to IWA-4530, "Repairs to welds that join P-No. 8 or P-No. 43 material to P-Nos. 1, 3, 12A, 12B, and 12C material may be made without the specified postweld heat treatment, provided the requirements of IWA-4530 through IWA-4533 are met. Repairs made to this paragraph are limited to those along the fusion line of a nonferritic weld to ferritic base material where 1/8 in. or less of nonferritic weld deposit exists above the original fusion line after defect removal."

BVPS requests relief to utilize the applicable sections of ASME Xl, 1989 Edition, 1991 Addenda; Code case N638; and the alternative methods described and supported by WCAP-15987-NP Rev. 1.

IV. Proposed Alternative A. Background The RPV head penetration nozzles at BVPS Units 1 and 2 are considered to have a moderate susceptibility to Primary Water Stress Corrosion Cracking (PWSCC). This is based upon a susceptibility ranking of MRP-75.

Should repair welding of RPV head penetration nozzle J-welds encroach (within 1/8-inch) on the ferritic base material of the RPV head, temper bead weld repairs would be required. See the following figures for additional details.

"* Figure 1: Typical RPV Head Penetration Nozzle

"* Figure 2: Example Repair of an RPV Head Penetration Nozzle J-Weld B. Proposed Alternative Pursuant to 10 CFR 50.55a(a)(3)(i), BVPS proposes alternatives to the GTAW-machine temper bead welding requirements of IWA-4500 and IWA-4530 of ASME Section X1, 1989 Edition, 1991 Addenda. Specifically, BVPS proposes to perform ambient temperature temper bead welding in accordance with Attachment 1 to this letter, "Dissimilar Metal Welding Using Ambient Temperature Machine GTAW Page 2 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Temper Bead Technique," as an alternative to IWA-4500 and IWA-4530.

BVPS has reviewed the proposed ambient temperature temper bead welding techniques of Attachment 1 against the GTAW-machine temper bead welding requirements of IWA-4500 and IWA-4530. This review was performed to identify differences between Attachment 1 and IWA-4500 and IWA-4530. Based upon this review, BVPS proposes alternatives to the following ASME Section XI requirements of IWA-4500 and IWA-4530 (1989 Edition, 1991 Addenda):

1. IWA-4500(a) specifies that repairs to base materials and welds identified in IWA-4530 may be performed without the specified postweld heat treatment of the construction code or ASME Section III provided the requirements of IWA-4500 and IWA-4530 are met. IWA-4530 includes temper bead requirements applicable to the Shielded Metal Arc Welding (SMAW) and the machine or automatic GTAW processes. As an alternative, BVPS proposes to perform temper bead weld repairs using the ambient temperature temper bead technique described in Attachment 1. Only the machine or automatic GTAW process can be used when performing ambient temperature temper bead welding in accordance with Attachment 1.
2. IWA-4500(d)(2) specifies that if repair welding is to be performed where physical obstructions impair the welder's ability to perform, the welder shall also demonstrate the ability to deposit sound weld metal in the positions, using the same parameters and simulated physical obstructions as are involved in the repair. This limited accessibility demonstration applies when manual temper bead welding is performed using the SMAW process. It does not apply to "welding operators" who perform machine or automatic GTAW welding from a remote location. (This distinction is clearly made in IWA-4500 and IWA-4530.)

Because the proposed ambient temperature temper bead technique described in Attachment 1 utilizes a machine GTAW welding process, limited access demonstrations of "welding operators" are not required. Therefore, the requirement of IWA-4500(d)(2) does not apply.

3. IWA-4500(e)(2) specifies that the weld area plus a band around the repair area of at least 11/2/2 times the component thickness or 5 inches, whichever is less, shall be preheated and maintained at a minimum temperature of 300OF for the0 GTAW process during welding; maximum interpass temperature shall be 450 F.

As an alternative, BVPS proposes that the weld area plus a band around the repair area of at least 11/2 times the component thickness or 5 inches, whichever is less, shall be preheated and maintained at a minimum temperature of 50°F for the GTAW process during welding; maximum interpass temperature shall be 150OF for the 1/8-inch butter thickness (first three weld layers as a minimum) and 350°F for the balance of welding.

Relief Request BV3-RV-03 Page 3 18 3 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements

4. IWA-4500(e)(2) specifies that thermocouples and recording instruments shall be used to monitor process temperatures. As an alternative, BVPS proposes to monitor preheat and interpass temperatures using an infrared thermometer.
5. IWA-4500(e)(2) specifies that thermocouple attachment and removal shall be performed in accordance with ASME Section II1. Because BVPS will use an infrared thermometer to monitor preheat and interpass temperatures, thermocouples will not be used. Therefore, the thermocouple attachment and removal requirements of IWA-4500(e)(2) do not apply.
6. IWA-4532.1 establishes procedure technique requirements that apply when using the SMAW process. Because the proposed ambient temperature temper bead technique of Attachment 1 utilizes the machine or automatic GTAW welding process, the SMAW temper bead technique requirements of paragraph IWA-4532.1 do not apply.
7. IWA-4532.2 establishes procedure technique requirements that apply when using the GTAW process but do not address joint design qualification of the repair cavity. As an alternative, BVPS proposes to control the joint design of the proposed repair cavity by requiring that the root width and included angle of the repair cavity in the test assembly be no greater than the minimum specified for the repair.
8. IWA-4532.2(c) specifies that the repair cavity shall be buttered with the first six layers of weld metal in which the heat input of each layer is controlled to within

+/-10% of that used in the procedure qualification test, and heat input control for subsequent layers shall be deposited with a heat input equal to or less than that used for layers beyond the sixth in the procedure qualification. As an alternative, BVPS proposes to butter the weld area with a minimum of three layers of weld metal to obtain a minimum butter thickness of 1/8-inch. The heat input of each weld layer in the 1/8-inch thick buttered section shall be controlled to within

+/-10% of that used in the procedure qualification test. The heat input for subsequent weld layers shall not exceed the heat input used for layers beyond the 1/8-inch thick buttered section (first three weld layers) in the procedure qualification. The basis for this alternative has been documented in WCAP 15987-P Rev. 1.

9. IWA-4532.2(c) specifies that the completed weld shall have at least one layer of weld reinforcement deposited and then this reinforcement shall be removed by mechanical means. As an alternative, the proposed ambient temperature temper bead technique does not include a reinforcement layer.
10. IWA-4532.2(d) specifies that, after at least 3/16-inch of weld metal has been deposited, the weld area shall be maintained at a temperature of 300OF (minimum) for a minimum of four (4) hours (for P-No. 3 materials). As an Page 4 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements alternative, the proposed ambient temperature temper bead technique does not include a postweld soak.

11. IWA-4532.2(e) specifies that after depositing at least 3/16-inch of weld metal and 0

performing a postweld soak at a minimum temperature of 300 F, the balance of 0

welding may be performed at an interpass temperature of 350 F. As an alternative, BVPS proposes that an interpass temperature of 350°F may be used after depositing at least 1/8-inch of weld metal without a postweld soak.

12. IWA-4533 specifies the following examinations shall be performed after the completed repair weld has been at ambient temperature for at least 48 hour5.555556e-4 days <br />0.0133 hours <br />7.936508e-5 weeks <br />1.8264e-5 months <br />s:

(a) the repair weld and preheated band shall be examined by the liquid penetrant method; (b) the repaired region shall be examined by the radiographic method, and if practical, (c) by the ultrasonic method. BVPS will perform the liquid penetrant examination of the completed repair weld and preheated band as required by IWA-4533. As an alternative to the volumetric examination of IWA-4533, BVPS proposes the following examinations for repair welds in RPV penetration nozzle J-welds.

Repair welds will be progressively examined by the liquid penetrant method in accordance with NB-5245 of ASME Section III. The liquid penetrant examinations will be performed in accordance with NB-5000. Acceptance criteria shall be in accordance with NB-5350.

This request for alternative is specific to localized weld repair of RPV head penetration nozzle J-welds where 1/8-inch or less of Inconel weld metal exists between the J-weld repair cavity and the ferritic base material of the RPV head. See Figures 1 and 2. Flaws in the J-weld will be removed prior to performing any temper bead repairs in accordance with this relief request.

V. Basis of Alternative for Providing Acceptable Level of Quality and Safety The RPV heads are manufactured from P-Number 3, Group 3 low alloy steels. If repairs are performed in accordance with ASME Section III, BVPS would have two options: (1) perform a weld repair that includes a postweld heat treatment (PWHT) at 11 00°F - 12500 F in accordance with NB-4622.1; or (2) perform a temper bead repair using the SMAW process in accordance with NB-4622.1 1. Each option is discussed below.

1. PWHT of the RPV head is an impractical option that would permanently damage the RPV head assembly. ASME Section III NB-4600 requires PWHT to be performed at 11000 - 12500 F. PWHT of the RPV head will result in ovalization and misalignment of CRDM penetrations and changes in clearances.

Relief Request BV3-RV-03 18 of 18 Page 55 of Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements

2. NB-4622.1 1 provides temper bead rules for repair welding of dissimilar materials using the SMAW process. Because NB-4622.11 does not include temper bead rules for the machine or automatic Gas Tungsten Arc Welding (GTAW) process, a manual temper bead process must be used. However, a manual SMAW temper bead repair is not a desirable option due to radiological considerations.

First of all, scaffolding must be built and resistant heating blankets, thermocouples, and insulation must be installed. Secondly, the manual SMAW temper bead welding process is a time and dose intensive process. Each weld layer is manually deposited in a high dose and high temperature (3500 F) environment. The manual SMAW temper bead process of NB-4622.11 also requires that the weld crown of the first weld layer be mechanically removed by grinding. Upon completing repair welding, resistant heating blankets, thermocouples, insulation, and scaffolding must be removed. Thermocouples and heating blanket mounting pins must be removed by grinding. The ground areas must be subsequently examined by the magnetic particle or liquid penetrant examination.

BVPS estimates that the dose associated with an SMAW temper bead repair on the RPV head to be at least 20 to 25 REM more than the proposed method of repair per weld repair. In addition, BVPS estimates the dose associated with the set-up and disassembly of the elevated preheat and postweld soak to be at least 15 REM.

ASME Section XI, 1989 Edition, IWA 4120 (b) states, "The Edition and Addenda of Section XI used for the repair program shall correspond with the Edition and Addenda identified in the inservice inspection program applicable to the inspection interval." In addition, IWA 4120 (c) of the same Edition and Addenda states, "Later Editions and Addenda of Section XI, either in their entirety or portions thereof, may be used for the repair program, provided these Editions and Addenda of Section XI at the time of the planned repair have been incorporated by reference in amended regulations of the regulatory authority having jurisdiction at the plant site. BVPS requests approval for the use of portions of ASME XI, 1989 Edition, 1991 Addenda, the use of Code case N638, and the alternative methods listed below, as applicable, to complete VHP repairs during the spring 2003 outage and for the remaining life of the Bv-1 existing Reactor head component.

BVPS has not requested an alternative to NB-4622.1 1; rather, this request proposes an alternative to IWA-4500 and IWA-4530 of the ASME Section XI, 1989 Edition, 1991 Addenda. Owners are allowed by ASME Section Xl IWA-4170(b) and IWA 4500(a) to perform temper bead repairs of dissimilar materials. IWA-4170(b) and IWA-4500(a) provide requirements and controls for performing such repairs.

IWA-4500 and IWA-4530 of ASME Section XI, 1989 Edition, 1991 Addenda, establish requirements for performing temper bead welding of "dissimilar materials".

According to IWA-4530, either the automatic or machine GTAW process or SMAW process may be used. When using the machine GTAW process, a minimum preheat temperature of 300L-F must be established and maintained throughout the Page 6 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements 2

welding process while the interpass temperature is limited to 450 F. Upon completion of welding, a postweld soak is performed at 300°F (minimum) for a minimum of 4 hours4.62963e-5 days <br />0.00111 hours <br />6.613757e-6 weeks <br />1.522e-6 months <br />.

The IWA-4500 and IWA-4530 temper bead welding process is a time and dose intensive process. Resistant heating blankets are attached to the RPV head; typically a capacitor discharge stud welding process is used. Thermocouples must also be attached to the RPV head using a capacitor discharge welding process to monitor preheat, interpass, and postweld soak temperatures. Prior to heat-up, thermal insulation is also installed. Upon completion of repair welding (including the postweld soak), the insulation, heating blankets, studs, and thermocouples must be removed from the RPV head. Thermocouples and stud welds are removed by grinding. Ground removal areas are subsequently examined by the liquid penetrant or magnetic particle method. A significant reduction in dose could be realized by utilizing an ambient temperature temper bead process. Because the ASME Code does not presently include rules for ambient temperature temper bead welding, BVPS proposes the alternative described in EPRI Report GC-1 11050.

A. Evaluation of the Ambient Temperature Temper Bead Technique Automatic or machine temper bead welding procedures without preheat will produce satisfactory toughness and ductility properties both in the weld and weld heat affected zones. The results of previous industry qualifications and repairs support this conclusion. The use of an ambient temperature temper bead welding procedure will improve the feasibility of performing localized weld repairs with a significant reduction in radiological exposure.

B. Evaluation of Proposed Alternatives to ASME Section XI, IWA-4500 and IWA-4530 (1989 Edition, 1991 Addenda)

1. According to IWA-4500(a), repairs may be performed to dissimilar base materials and welds without the specified postweld heat treatment of ASME Section III provided the requirements of IWA-4500 and IWA-4530 are met.

The temper bead rules of IWA-4500 and IWA-4530 apply to dissimilar materials such as P-No. 43 to P-No. 3 base materials welded with F-No. 43 filler metals. When using the GTAW-machine process, the IWA-4500 and IWA-4530 temper bead process is based fundamentally on an elevated 0 preheat temperature of 3000 F, a maximum interpass temperature of 450 F, and a postweld soak of 300°F. The proposed alternative of Attachment 1 also establishes requirements to perform temper bead welding on dissimilar material welds that join P-No. 43 to P-No. 3 base materials using F-No. 43 filler metals. However, the temper bead process of Attachment 1 is an ambient temperature technique which only utilizes the GTAW-machine or GTAW-automatic process. The suitability of the proposed ambient Page 7 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements temperature temper bead technique is evaluated in this section. The results of this evaluation demonstrate that the proposed ambient temperature temper bead technique provides an acceptable level of quality and safety.

2. According to IWA-4500(e)(2), the weld area plus a band around the repair area of at least 1-1/2 times the component thickness or 5 inches, whichever is less, shall be preheated and maintained at a minimum temperature of 300OF for the GTAW process during welding while the maximum interpass temperature is limited to 4500 F. The ambient temperature temper bead technique of Attachment 1 also establishes a preheat band of at least 11/2 times the component thickness or 5 inches, whichever is less. However, the ambient temperature temper bead technique requires a minimum preheat temperature of 50 0 F, a maximum interpass temperature of 150OF for the first three layers, and a maximum interpass temperature of 350°F for the balance of welding. The suitability of an ambient temperature temper bead technique with reduced preheat and interpass temperatures is addressed in Section V.A.
3. According to IWA-4500(e)(2), thermocouples and recording instruments shall be used to monitor process temperatures. As an alternative to IWA-4500(e)(2), BVPS proposes to monitor preheat and interpass temperatures using an infrared thermometer. Infrared thermometers are hand-held devices that can be used to monitor process temperature from a remote location. To determine the preheat and interpass temperatures during the welding operation, the infrared thermometer is pointed at a target location adjacent to the repair weld. The target location is identified by a circle consisting of eight laser spots. A single laser spot in the center of the circle identifies the center of the measurement area. As the distance (D) from the object being measured increases, the diameter of the target location or "spot size" (S) also increases. The optics of the infrared thermometer sense emitted, reflected, and transmitted energy from the target location that is collected and focused onto a detector. The infrared thermometer's electronics translate the information into a temperature reading that is displayed on the unit. The infrared thermometer measures the maximum, minimum, differential, and average temperatures across the target location. This data can be stored and recalled until a new measurement is taken. BVPS plans to use an infrared thermometer such as the Raytek Raynger ST80 (or equivalent). The Raytek Raynger ST80 infrared thermometer measures temperatures from -25°F to 1400OF over the target location with the following accuracy: +/-30 F over the 0°F - 73 0 F temperature range and +/-1 % of reading or 21F, whichever is greater, above 73 0F. Display resolution is 0.1IF. The distance (D) to "spot size" (S) is 50:1 for the Raytek Raynger ST80 infrared thermometer. Since the "distance" (D) to the target location on the RPV penetration nozzle or J-weld is estimated to range from 3 feet to 6 feet, the "spot size" (S) will also range Page 8 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements from 0.72 inch to 2.22 inches. The infrared thermometer will be appropriately calibrated prior to use.

4. IWA-4532.2 establishes procedure technique requirements but do not address joint design access qualification of the repair cavity. As an alternative to IWA-4532.2, BVPS proposes to control the root width and included angle of the proposed repair cavity. Paragraph 2.1(c) of Attachment 1 requires that the root width and included angle of the repair cavity in the test assembly be no greater than the minimum specified for the repair. This requirement ensures that the welding procedure is only used in repair cavity configurations where it has demonstrated capability (i.e.

sufficient access to deposit root passes, tie-in to the beveled or tapered walls of the repair cavity, provide appropriate tempering, and ensure complete weld fusion).

5. According to IWA-4532.2(c), the repair cavity shall be buttered with six layers of weld metal in which the heat input of each layer is controlled to within +/-10% of that used in the procedure qualification test, and heat input control for subsequent layers shall be deposited with a heat input equal to or less than that used for layers beyond the sixth in the procedure qualification.

As an alternative to IWA-4532.2, BVPS proposes to butter the repair cavity or weld area with at least three layers of weld metal to obtain a minimum butter thickness of 1/8-inch. The heat input of each layer in the 1/8-inch thick buttered section shall be controlled to within +/-10% of that used in the procedure qualification test. The heat input for subsequent weld layers shall not exceed the heat input used for layers beyond the 1/8-inch thick buttered section (first three weld layers) in the procedure qualification. When using the ambient temperature temper bead technique of Attachment 1, the machine GTAW process is used. Machine GTAW is a low heat input process that produces consistent small volume heat affected zones.

Subsequent GTAW weld layers introduce heat into the heat affected zone produced by the initial weld layer. The heat penetration of subsequent weld layers is applied to produce overlapping thermal profiles that develop a correct degree of tempering in the underlying heat affected zone. When welding dissimilar materials with nonferritic weld metal, the area requiring tempering is limited to the weld heat affected zone of the ferritic base material along the ferritic fusion line.

After buttering the ferritic base material with at least 1/8-inch of weld metal (first 3 weld layers), subsequent weld layers should not provide any additional tempering to the weld heat affected zone in the ferritic base material. Therefore, less restrictive heat input controls are adequate after depositing the 1/8-inch thick buttered section. It should also be noted that IWA-4530 does not require temper bead welding except "where 1/8-inch or less of nonferritic weld deposit exists above the original fusion line after defect removal". The proposed heat input techniques of Attachment 1 were Page 9 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements utilized in the qualification of Welding Procedure Specification (WPS) 3 43/52-TB MC-GTAW-N638. Based on Charpy V-notch testing of the procedure qualification test coupon, impact properties in weld heat affected zone were superior to those of the unaffected base material. Therefore, the proposed heat input controls of Attachment 1 provide an appropriate level of tempering. Test results of the WPS qualification are provided in Section V.C.

6. According to IWA-4532.2(c), at least one layer of weld reinforcement shall be deposited on the completed weld and with this reinforcement being subsequently removed by mechanical means. In the proposed alternative of Attachment 1, the deposition and removal of a reinforcement layer is not required. A reinforcement layer is required when a weld repair is performed to a ferritic base material or ferritic weld using a ferritic weld metal. On ferritic materials, the weld reinforcement layer is deposited to temper the last layer of untempered weld metal of the completed repair weld. Because the weld reinforcement layer is untempered (and unnecessary), it is removed. However, when repairs are performed to dissimilar materials using nonferritic weld metal, a weld reinforcement layer is not required because nonferritic weld metal does not require tempering. When performing a dissimilar material weld with a nonferritic filler metal, the only location requiring tempering is the weld heat affected zone in the ferritic base material along the weld fusion line. However, the three weld layers of the 1/8-inch thick butter section are designed to provide the required tempering to the weld heat affected zone in the ferritic base material.

Therefore, a weld reinforcement layer is not required. While BVPS recognizes that IWA-4532.2(c) does require the deposition and removal of a reinforcement layer on repair welds in dissimilar materials, BVPS does not believe that this reinforcement layer is necessary. This position is supported by the fact that ASME Code Case N-638 only requires the deposition and removal of a reinforcement layer when performing repair welds on similar (ferritic) materials. Repair welds on dissimilar materials are exempt from this requirement.

7. According to IWA-4532.2(d), the weld area shall be maintained at a minimum temperature of 3001F for a minimum of 4 hours4.62963e-5 days <br />0.00111 hours <br />6.613757e-6 weeks <br />1.522e-6 months <br /> (for P-No. 3 materials) after at least 3/16-inch of weld metal has been deposited. In the proposed alternative of Attachment 1, a postweld soak is not required. The suitability of an ambient temperature temper bead technique without a postweld soak is addressed in Section V.A.
8. According to IWA-4532.2(e), after depositing at least 3/16-inch of weld metal and performing a postweld soak at a minimum temperature of 300 0 F, the balance of welding may be performed at an interpass temperature of 350 0 F. As an alternative, BVPS proposes that an interpass temperature of Page 10 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements 350°F may be used after depositing at least 1/8 inch of weld metal without a postweld soak. The proposed ambient temperature temper bead process of Attachment 1 is carefully designed and controlled such that successive weld beads supply the appropriate quantity of heat to the untempered heat affected zone such that the desired degree of carbide precipitation (tempering) is achieved. The resulting microstructure is very tough and ductile. This point is validated by the qualification of WPS 3-43/52-TB MC GTAW-N638. Based on Charpy V-notch testing of the procedure qualification test coupon, impact properties in weld heat affected zone were superior to those of the unaffected base material. Test results of the WPS qualification are provided in Section IV.C. The suitability of an ambient temperature temper bead technique without a postweld soak is addressed in Section V.A.

9. IWA-4533 specifies that the repair weld shall be volumetrically examined by the radiographic method, and if practical, by the ultrasonic method after the completed repair weld has been at ambient temperature for at least 48 hours5.555556e-4 days <br />0.0133 hours <br />7.936508e-5 weeks <br />1.8264e-5 months <br />. As an alternative to the volumetric examinations of IWA-4533, BVPS proposes the examinations of repair welds in RPV penetration nozzle J welds described below. The suitability of the alternative examinations is addressed in Section V.D.

Repair welds will be progressively examined by the liquid penetrant method in accordance with NB-5245 of ASME Section II1. The liquid penetrant examinations will be performed in accordance with NB-5000.

Acceptance criteria shall be in accordance with NB-5350.

C. Mechanical Properties of WPS 3-43/52-TB MC-GTAW-N638 WPS 3-43/52-TB MC-GTAW-N638 was qualified in accordance with Attachment 1. The welding procedure qualification test assembly was 3 inches thick and consisted of SA-533, Grade B, Class 1 (P-No. 3, Group 3) and SB 166, N06690 (P-No. 43) base materials. Prior to welding, the SA-533, Grade B, Class 1 portion of the test assembly was heat treated for 40 hours4.62963e-4 days <br />0.0111 hours <br />6.613757e-5 weeks <br />1.522e-5 months <br /> at 1,200 0 F.

The repair cavity in the test assembly was 1.5 inches deep. The test assembly cavity was welded in the 3G (vertical) position using ERNiCrF3-7 (F-No. 43) filler metal. Results of the welding procedure qualification were documented on procedure qualification record PQR 707. Results of mechanical testing tensile testing, bend testing, Charpy V-notch testing, and drop weight testing are summarized below. WPS 3-43/52-TB MC-GTAW-N638 will be used to perform the repair welding activities described in Section IV.B.

Tensile test specimens exhibited a tensile strength that exceeded 80,000 psi and were acceptable per ASME Section IX. The bend testing was also acceptable. Test results are as follows:

Page 11 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Tensile Test Results Specimen Tensile Actual Tensile Failure No. Specimen Strength Test 1-1 0.505" Turned Specimen 86,600 psi Ductile/Base Test 1-2 0.505" Turned Specimen 84,500 psi Ductile/Base Test 2-3 0.505" Turned Specimen 82,400 psi Fusion Line Test 2-4 0.505" Turned Specimen 86,600 psi Ductile/Weld Metal Bend Test Results Specimen Type and Figure No. Result Side Bend 1 QW-462.2 Acceptable Side Bend 2 QW-462.2 Acceptable Side Bend 3 QW-462.2 Acceptable Side Bend 4 QW-462.2 Acceptable

° Drop weight and Charpy V-notch testing of the SA-533, Grade B, Class 1 "unaffected" base material was performed. Based upon drop weight testing of the SA-533, Grade B, Class 1 "unaffected" base material, a nil ductility transition temperature (TNDT) of -50OF was established. Charpy V-notch testing was also performed at +10 0 F. All three Charpy V-notch specimens exhibited at least 35 mils and 50 ft-lbs. Based upon the above testing, an RTNDT of -50OF was established for the SA-533, Grade B, Class 1 base material. Test results are as follows:

Relief Request BV3-RV-03 18 of 18 12 of Page 12 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Drop Weight Test: Unaffected Base Material Specimen Specimen Test Drop Weight ID Type Temperature Break TNDT DW1 P-3 -40OF No -50OF DW2 P-3 -40°F No -50'F Charpy V-Notch Tests: Unaffected Base Material Specimen Test Absorbed' Lateral  % Shear ID Temperature Energy (ft-lbs) Expansion(mils) Fracture 1 +10°F 59.0 50.0 60.0 2 +10°F 51.0 43.0 50.0 3 +10°F 50.0 45.0 50.0 Average +10°F 53.3 46.0 53.3 Charpy V-notch testing of the SA-533, Grade B, Class 1 heat affected zone was also performed at +10F. The absorbed energy, lateral expansion, and percent shear fracture of the heat affected zone test specimens were compared to the test values of the unaffected base material specimens.

The average values of the three heat affected zone specimens were greater than those of the unaffected base material specimens. Based upon these results, it is clear that the proposed ambient temperature temper bead process improved the heat affected zone properties. Test results are as follows:

Charpy V-Notch Tests: Heat Affected Zone Specimen Test Absorbed . Lateral  % Shear ID Temperature Energy (ft-lbs) - Expansion(mils) Fracture 1 +10°F 85.0 65.0 90.0 2 +10°F 136.0 64.0 75.0 3 +10°F 124.0 49.0 30.0 A verage +10°F 115.0 59.3.0 65.0 Supplemental microstructural evaluations were also performed on the test coupon weld of the procedure qualification. Microstructural evaluations consisted of micro-hardness testing (Vickers) and metallography. Vickers micro-hardness testing was performed at three different locations:

1. 0.125 inch below the surface of the weld,
2. 0.625 inch below the surface of the weld, and
3. 0.125 inch above the root of the weld.

Micro-hardness test values are provided in the table below.

Page 13 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Metallography was performed at 1OOX and 500X magnifications. According to CONAM Laboratory Report #2333, "There were a few colonies of tempered martensite observed near the root of the weld. These seem to be associated with the slight banding present in the base material. There was no indication of untempered martensite. The remaining areas of the heat affected zone consist of a mixed microstructure of by-products of high temperature pearlite degeneration, bainite and a small amount of ferrite." Regarding the presence of carbides, the CONAM report stated, "There was no evidence of massive carbides or carbide networks."

Vickers Micro-Hardness Tests Results Weld Zone Location 0.125" 0.625" 0.125" From Surface From Surface Above Weld Root Filar Vickers Filar Vickers Filar Vickers 182 224 184 219 182 224 Unaffected 182 224 185 217 176 240 Base 183 222 186 214 174 245 Material 182 224 186 214 181 226 184 219 182 224 178 234 184 219 187 212 173 248 167 266 162 283 150 330 HAZ 165 273 164 276 144 358 Grain Coarsened Region 165 273 169 260 144 358 163 279 161 287 149 334 HAZ 161 287 161 287 147 343 Adjacent to Fusion Line 159 293 164 276 147 343 183 222 187 212 190 205 Weld 189 208 192 201 189 208 Metal 184 219 185 217 186 214 184 219 185 217 182 224 189 208 183 222 182 224 193 199 184 219 179 232 D. Suitability of Alternative Nondestructive Examinations (NDE)

IWA-4533 specifies that the repaired region shall be examined by the radiographic method, and if practical, by the ultrasonic method. The NDE requirements of IWA-4533 were established based upon a temper bead weld repair to butt welds. Figures IWA-4532.1-1 and IWA-4532.2-1 clearly indicate this. While the requirement to perform a radiographic examination, and if practical, an ultrasonic examination of a butt weld between a nozzle and pipe is appropriate, these examinations are not appropriate for weld repairs of RPV head penetration nozzle J-welds. See Figures 1 and 2.

Page 14 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements

1. Impracticality of Volumetric Examinations Radiographic examination of weld repairs of RPV head penetration nozzle J-welds is not practical. Meaningful radiographic examination cannot be performed due to the weld configuration and access limitations. The weld configuration and geometry of the penetration in the head provide an obstruction for the radiography and interpretation would be very difficult.

Ultrasonic examination of the J-weld would also be impractical.

2. Suitability of Proposed Alternative As an alternative to radiographic and ultrasonic examinations, BVPS proposes to perform a progressive liquid penetrant of the J-weld repair weld in accordance with NB-5245 of ASME Section III. It should be noted that ASME Section III does not require volumetric examination of J-welds.

According to NB-3352.4(d)(1), "partial penetration welds used to connect nozzles as permitted in NB-3337.3 shall meet the fabrication requirements of NB-4244(d) and shall be capable of being examined in accordance with NB-5245." NB-4244(d) establishes fabrication details for nozzles welded with partial penetration welds as shown in Figures NB-4244(d)-1 and NB-4244(d)-2.

According to NB-5245, "Partial penetration welds, as permitted in NB-3352.4(d), and as shown in Figures NB-4244(d)-1 and NB-4244(d)-2, shall be examined progressively using either the magnetic particle or liquid penetrant method. The increments of examination shall be the lesser of one-half of the maximum weld dimension measured parallel to the centerline of the connection or 1/2-inch. The surface of the finished weld shall also be examined by either method."

The partial penetration J-welds of the RPV head penetration nozzles were designed and fabricated in accordance with NB-3352.4(d) and NB-4244(d).

Therefore, according to NB-3352.4(d), the code required examination for these partial penetration J-welds is a progressive liquid penetrant examination performed in accordance with NB-5245. A volumetric examination is not required.

VI. CONCLUSION 10 CFR 50.55a(a)(3) states:

"Proposed alternatives to the requirements of paragraphs (c), (d), (e), (f), (g), and (h) of this section or portions thereof may be used when authorized by the Director of the Office of Nuclear Reactor Regulation. The applicant shall demonstrate that:

Page 15 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements (i) The proposed alternatives would provide an acceptable level of quality and safety, or (ii) Compliance with the specified requirements of this section would result in hardship or unusual difficulty without a compensating increase in the level of quality and safety."

BVPS believes that compliance with the repair rules as stated in Reference 1 and as described in Section III of this request would result in unwarranted damage to the RPV head assembly. The proposed alternative discussed in Section IVwould provide an acceptable level of quality and safety without exposing the head to potential ovalization and misalignment of the CRDM penetrations. Additionally, the work required to meet the current Code repair method, automatic or machine GTAW temper bead with 300°F minimum preheat and 300°F post weld hydrogen bake-out, would be extremely difficult and the radiation exposures for set-up, monitoring, and removal of the required equipment is unjustified. Using the proposed method of repair, it is estimated that approximately 15 person-rem could be saved on each required repair. Therefore, we request that the proposed alternative be authorized pursuant to 10 CFR 50.55a(a)(3)(i).

VII. References

1. ASME Section XI, 1989 Edition
2. ASME Section XI, 1989 Edition, 1991 Addenda
3. ASME Section III, 1971 Edition, Winter 1973 Addenda
4. ASME Section III, Subsection NB, 1971 Edition, Summer 1973 Addenda
5. ASME Section III, Subsection NB, 1974 Edition, Winter 1975 Addenda
6. ASME Section XI Code Case N-638, "Similar and Dissimilar Metal Welding Using Ambient Temperature Machine GTAW Temper Bead Technique"
7. EPRI Report GC-1 11050, "Ambient Temperature Preheat for Machine GTAW Temper Bead Applications"
8. Letter 102-04603-CDM/SAB/RJR, "Response to NRC Bulletin 2001-01; Circumferential Cracking of VHP Nozzles," dated September 4, 2001
9. CONAM Inspection Laboratory Report #2333, dated July 23, 2002 10.WCAP-15987-P Rev.1, "Technical Basis for the Embedded Flaw Process for Repair of Reactor Vessel Head Penetrations" Page 16 of 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Typical Alloy 600 Nozzle Reactor Vessel Upper Head Stainless steel -Inconel 182 cladding B uttering "Inconel 182 Weld (J-Weld)

Typical RPV Head Penetration Nozzle FIGURE 1 Relief Request BV3-RV-03 Page 17 of 18 18 Relief Request BV3-RV-03

Proposed Alternatives to the Gas-Tungsten Arc Welding (GTAW) Machine Temper Bead Welding Requirements Example Repair of an RPV Head Penetration Nozzle J-Weld FIGURE 2 Page 18 of 18 Relief Request BV3-RV-03

ATTACHMENT 1 DISSIMILAR METAL WELDING USING AMBIENT TEMPERATURE MACHINE GTAW TEMPER BEAD TECHNIQUE

DISSIMILAR METAL WELDING USING AMBIENT TEMPERATURE MACHINE GTAW TEMPER BEAD TECHNIQUE 1.0 GENERAL REQUIREMENTS:

(a) The maximum area of an individual weld based on the finished surface will be less than 100 square inches, and the depth of the weld will not be greater than one-half of the ferritic base metal thickness.

(b) Repair/replacement activities on a dissimilar-metal weld are limited to those along the fusion line of a nonferritic weld to ferritic base material on which 1/8-inch or less of nonferritic weld deposit exists above the original fusion line. Repair/replacement activities on nonferritic base materials where the repair cavity is within 1/8-inch of a ferritic base material may also be performed.

(c) If a defect penetrates into the ferritic base material, repair of the base material, using a nonferritic weld filler material, may be performed provided the depth of repair in the base material does not exceed 3/8-inch.

(d) Prior to welding, the temperature of the area to be welded and a band around the area of at least 11/2 times the component thickness (or 5 inches, whichever is less) will be at least 50 0 F.

(e) Welding materials will meet the Owner's Requirements and the Construction Code and Cases specified in the repair/replacement plan. Welding materials will be controlled so that they are identified as acceptable until consumed.

(f) The area prepared for welding shall be suitably prepared for welding in accordance with a written procedure.

2.0 WELDING QUALIFICATIONS The welding procedures and the welding operators shall be qualified in accordance with Section IXand the requirements of paragraphs 2.1 and 2.2.

2.1 Procedure Qualification:

(a) The base materials for the welding procedure qualification will be the same P-Number and Group Number as the materials to be welded. The materials shall be post weld heat treated to at least the time and temperature that was applied to the material being welded.

Page 1 of 6 Attachment 1 to Relief Request BV3-RV-03

DISSIMILAR METAL WELDING USING AMBIENT TEMPERATURE MACHINE GTAW TEMPER BEAD TECHNIQUE (b) Consideration will be given to the effects of irradiation on the properties of material, including weld material for applications in the core belt line region of the reactor vessel. Special material requirements in the Design Specification will also apply to the test assembly materials for these applications.

(c) The root width and included angle of the cavity in the test assembly will be no greater than the minimum specified for the repair.

(d) The maximum interpass temperature for the first three layers or as required to achieve the 1/8-inch butter thickness in the test assembly will be 150 0 F. For the balance of the welding, the maximum interpass temperature shall be 3500 F.

(e) The test assembly cavity depth will be at least one-half the depth of the weld to be installed during the repair/replacement activity, and at least 1 inch. The test assembly thickness will be at least twice the test assembly cavity depth. The test assembly will be large enough to permit removal of the required test specimens. The test assembly dimensions surrounding the cavity will be at least the test assembly thickness, and at least 6 inches. The qualification test plate will be prepared in accordance with Figure 1.

(f) Ferritic base material for the procedure qualification test will meet the impact test requirements of the Construction Code and Owner's Requirements. If such requirements are not in the Construction Code and Owner's Requirements, the impact properties shall be determined by Charpy V-notch impact tests of the procedure qualification base material at or below the lowest service temperature of the item to be repaired. The location and orientation of the test specimens shall be similar to those required in subparagraph (h) below, but shall be in the base metal.

(g) Charpy V-notch tests of the ferritic weld metal of the procedure qualification shall meet the requirements as determined in subparagraph (f) above.

(h) Charpy V-notch tests of the ferritic heat-affected zone (HAZ) will be performed at the same temperature as the base metal test of subparagraph (f) above. Number, location, and orientation of test specimens will be as follows:

Page 2 of 6 Attachment 1 to Relief Request BV3-RV-03

DISSIMILAR METAL WELDING USING AMBIENT TEMPERATURE MACHINE GTAW TEMPER BEAD TECHNIQUE

1. The specimens will be removed from a location as near as practical to a depth of one-half the thickness of the deposited weld metal. The test coupons for HAZ impact specimens will be taken transverse to the axis of the weld and etched to define the HAZ. The notch of the Charpy V-notch specimens will be cut approximately normal to the material surface in such a manner as to include as much HAZ as possible in the resulting fracture. When the material thickness permits, the axis of a specimen will be inclined to allow the root of the notch to be aligned parallel to the fusion line.
2. Ifthe test material is in the form of a plate or a forging, the axis of the weld will be oriented parallel to the principal direction of rolling or forging.
3. The Charpy V-notch test will be performed in accordance with SA-370. Specimens will be in accordance with SA 370, Figure 11, Type A. The test will consist of a set of three full-size 10 mm x 10 mm specimens. The lateral expansion, percent shear, absorbed energy, test temperature, orientation and location of all test specimens will be reported in the Procedure Qualification Record.

(i) The average values of the three HAZ impact tests will be equal to or greater than the average values of the three unaffected base metal tests.

2.2 Performance Qualification:

Welding operators will be qualified in accordance with ASME Section IX.

3.0 WELDING PROCEDURE REQUIREMENTS:

The welding procedure shall include the following requirements:

(a) The weld metal shall be deposited by the automatic or machine GTAW process using cold wire feed.

(b) Dissimilar metal welds shall be made using F-No. 43 weld metal (QW-432) for P-No. 43 to P-No. 3 weld joints.

(c) The area to be welded will be buttered with a deposit of at least three layers to achieve at least 1/8-inch butter thickness as shown in Figure 2, steps 1 through 3, with the heat input for each layer Page 3 of 6 Attachment 1 to Relief Request BV3-RV-03

DISSIMILAR METAL WELDING USING AMBIENT TEMPERATURE MACHINE GTAW TEMPER BEAD TECHNIQUE controlled to within +/- 10% of that used in the procedure qualification test. Particular care will be taken in placement of the weld layers at the weld toe area of the ferritic base material to ensure that the HAZ is tempered. Subsequent layers will be deposited with a heat input not exceeding that used for layers beyond the third layer (or as required to achieve the 1/8-inch butter thickness) in the procedure qualification.

(d) The maximum interpass temperature field applications will be 350°F regardless of the interpass temperature during qualification.

(e) Particular care will be given to ensure that the weld region is free of all potential sources of hydrogen. The surfaces to be welded, filler metal, and shielding gas shall be suitably controlled.

4.0 EXAMINATION

(a) Prior to welding, a surface examination will be performed on the area to be welded.

(b) Repair welds in RPV penetration nozzle J-welds shall be examined as follows:

Repair welds will be progressively examined by the liquid penetrant method in accordance with NB-5245 of ASME Section I1l. After the completed repair weld has been at ambient temperature for at least 48 hours5.555556e-4 days <br />0.0133 hours <br />7.936508e-5 weeks <br />1.8264e-5 months <br />, repair welds including the preheat band (1.5 times the component thickness or 5 inches, whichever is less) around the repair weld shall be examined by the liquid penetrant method. The liquid penetrant examinations will be performed in accordance with ASME Section III, NB-5000.

Acceptance criteria shall be in accordance with NB-5350.

(c) NDE personnel performing liquid penetrant examination will be qualified and certified in accordance with NB-5500.

5.0 DOCUMENTATION Use of this request shall be documented on NIS-2. Alternatively, repairs may be documented on Form NIS-2A as described in Code Case N-532 if prior approval is obtained from the NRC.

Page 4 of 6 Attachment 1 to Relief Request BV3-RV-03

DISSIMILAR METAL WELDING USING AMBIENT TEMPERATURE MACHINE GTAW TEMPER BEAD TECHNIQUE Discard Transverse Side Bend Reduced Section Tensile Transverse Side Bend HAZ Charpy

,'* V-Notch Transverse Side Bend Reduced Section Tensile Transverse Side Bend Discard GENERAL NOTE: Base Metal Charpy impact specimens are not shown.

Figure 1 - QUALIFICATION TEST PLATE Page 5 of 6 Attachment 1 to Relief Request BV3-RV-03

METAL WELDING USING AMBIENT TEMPERATURE DISSIMILAR DISSIMILAR METAL WELDING USING AMBIENT TEMPERATURE MACHINE GTAW TEMPER BEAD TECHNIQUE Duration of Proposed alternative Step 1: Deposit layer one with first layer weld parameters used in qualification.

Step 2: Deposit layer two with second layer weld parameters used in qualification. NOTE:

Particular care shall be taken in application of the second layer at the weld toe to ensure that the weld metal and HAZ of the base metal are tempered.

Step 3: Deposit layer three with third layer weld parameters used in qualification. NOTE:

Particular care shall be taken in application of the third layer at the weld toe to ensure that the weld metal and HAZ of the base metal are tempered.

Step 4: Subsequent layers to be deposited as qualified, with heat input less than or equal to that qualified in the test assembly. NOTE:

Particular care shall be taken in application of the fill layers to preserve the temper of the weld metal and HAZ.

GENERAL NOTE: The illustration above is for similar-metal welding using a ferritic filler material.

For dissimilar-metal welding, only the ferritic base metal is required to be welded using steps 1 through 3 of the temperbead welding technique.

Figure 2 - AUTOMATIC OR MACHINE GTAW TEMPER BEAD WELDING Page 6 of 6 Attachment 1 to Relief Request BV3-RV-03