05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable
Show incoming properties 
Category
LICENSEE EVENT REPORT (SEE ALSO AO RO), TEXT-SAFETY REPORT  and Licensee Event Report
ASME section
ASME Section XI +
Accession number
ML20083F691  +
Docket
05000324  +  and 00324  +
From
Carolina Power & Light Co. +, Dietz C +  and Pastva M +
Has query"Has query" is a predefined property that represents meta information (in form of a <a rel="nofollow" class="external text" href="https://www.semantic-mediawiki.org/wiki/Subobject">subobject</a>) about individual queries and is provided by <a rel="nofollow" class="external text" href="https://www.semantic-mediawiki.org/wiki/Help:Special_properties">Semantic MediaWiki</a>.
05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +, 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +  and 05000324/LER-1983-097-01, /01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable +
Issue date
December 22, 1983  +
LER number
97  +
LER year
1,983  +
Modification date"Modification date" is a predefined property that corresponds to the date of the last modification of a subject and is provided by <a rel="nofollow" class="external text" href="https://www.semantic-mediawiki.org/wiki/Help:Special_properties">Semantic MediaWiki</a>.
10:55:10, 14 December 2024  +
NRC bulletin
NRC Bulletin 83-02 +
Page count
3  +
Site
Brunswick +
Site license
Brunswick +
Start date
December 22, 1983  +
System
Residual Heat Removal +
TS
TS-6.9.1 +
Title
/01T-0:on 831212,during IE Bulletin 83-02 Testing, Crack Indications Identified in 19 of 131 Welds.Caused by Intergranular Stress Corrosion Cracking.Eight Welds Repaired.Remaining Indications Acceptable  +
To
James O'Reilly +  and NRC OFFICE OF INSPECTION & ENFORCEMENT (IE REGION II) +
Topic
Intergranular Stress Corrosion Cracking +  and Weld Overlay +
URL"URL" is a <a href="/Special:Types/URL" title="Special:Types/URL">type</a> and predefined property provided by <a rel="nofollow" class="external text" href="https://www.semantic-mediawiki.org/wiki/Help:Special_properties">Semantic MediaWiki</a> to represent URI/URL values.
https://lersearch.inl.gov/Index.aspx?Page=PDFView?Doc::3241983097R01.pdf  +  and http://pbadupws.nrc.gov/docs/ML2008/ML20083F691.pdf  +
 
Retrieved from "https://kanterella.com/Special:Browse/:05000324-2FLER-2D1983-2D097-2D01,-20-2F01T-2D0:on-20831212,during-20IE-20Bulletin-2083-2D02-20Testing,-20Crack-20Indications-20Identified-20in-2019-20of-20131-20Welds.Caused-20by-20Intergranular-20Stress-20Corrosion-20Cracking.Eight-20Welds-20Repaired.Remaining-20Indications-20Acceptable"